材料科学技术（英）
The effect of sputtered Ti-50Al-10Cr and Ti-50Al-20Cr coatings on both isothermal and cyclic oxidation resistance at 800 similar to 900 degreesC and hot corrosion resistance at 850 degreesC of Ti-24Al-14Nb-3V was investigated. Results indicated that Ti-24Al-14Nb-3V alloys exhibited poor oxidation resistance due to the formation of Al2O3+TiO2+AlNbO4 mixed scales in air at 800 similar to 900 degreesC and poor hot corrosion resistance due to the spallation of scales formed in Na2SO4+K2SO4 melts at 850 degreesC. Both Ti-50Al-10Cr and Ti-50Al-20Cr coatings remarkably improved the oxidation and hot corrosion resistance of Ti-24Al-14Nb-3V alloy.